en

Accelerated laboratory test of rubberwood oriented strandboard exposed to wood decay fungi Okino, Esmeralda Yoshico Arakaki; Del Menezzi, Cláudio Henrique Soares; Alves, Marcus Vinícius da Silva; Teixeira, Divino Eterno; de Souza, Mário Rabelo & Santana, Marcos Antonio Eduardo Abstract This work aimed to evaluate the natural durability of oriented strandboards (OSB) manufactured with strands of Hevea brasiliensis Müll.Arg. bonded with 5% and 8% of urea-formaldehyde (UF) and phenol-formadehyde (FF) resins, exposed to xilophagous fungi under laboratory conditions. In accelerated laboratory test decay, samples of OSB were exposed to the following fungi: the brown-rot fungi Gloeophyllum trabeum (Pers. ex Fries) Murr., Coniophora puteana (Schumach. : Fr.)P. Karst., Meruliporia incrassata (Berk. & M.A. Curtis) Murrill as well as the white-rot fungi Fomes annosus (Fr. : Fr.) Cooke, Trametes versicolor (L. : Fr.) Pilát, Ganoderma applanatum (Pers.) Pat., Bjerkandera fumosa (Pers. : Fr.) P. Karst. and Phanerochaete chrysosporium Burds. Among the brown-rot fungi, the Gloeophyllum trabeum was the most aggressive, showing the highest loss of mass. Trametes versicolor and Ganoderma applanatum confirmed the preference for broadleave species. All oriented strandboards at lower UF resin contents were more degraded by Phanerochaete chrysosporium, Trametes versicolor, Ganoderma applanatum, Merulia incrassata, Coniophora puteana and Gloeophyllum trabeum, with high rate of loss of mass. Coniophora puteana showed small loss of mass when FF resin was applied. Bjerkandera fumosa showed low loss of mass only at higher resin content. Oriented strandboards exposed to Coniophora puteana showed insignificant OSB degradation. Keywords natural durability; xilophagous fungi; Hevea brasiliensis; OSB

pt

Ensaio acelerado de laboratório de chapas osb de seringueira submetidas ao ataque de fungos apodrecedores Okino, Esmeralda Yoshico Arakaki; Del Menezzi, Cláudio Henrique Soares; Alves, Marcus Vinícius da Silva; Teixeira, Divino Eterno; de Souza, Mário Rabelo & Santana, Marcos Antonio Eduardo Resumo O objetivo do trabalho foi avaliar a resistência natural de chapas de partículas orientadas (OSB) confeccionadas com partículas de Hevea brasiliensis Müll.Arg. aderidas com as resinas sintéticas uréiaformaldeído (UF) e fenol-formaldeído (FF), a 5% e 8%, expostas a fungos xilófagos em condições de laboratório. No ensaio acelerado de laboratório as amostras foram submetidas ao ataque dos fungos de podridão-parda Gloeophyllum trabeum (Pers. : Fr.) Murril, Coniophora puteana (Schumach. : Fr.) P. Karst., Meruliporia incrassata (Berk. & M.A. Curtis) Murrill e também aos fungos de podridão-branca, Fomes annosus (Fr. : Fr.) Cooke, Trametes versicolor (L. : Fr.) Pilát, Ganoderma applanatum (Pers.) Pat., Bjerkandera fumosa (Pers. : Fr.) P. Karst. e Phanerochaete chrysosporium Burds. Dentre os fungos de podridão-parda, o Gloeophyllum trabeum causou a maior perda de massa nos corpos-de-prova testados. Dentre os fungos de podridão-branca, Trametes versicolor, Phanerochaete chrysosporium e Ganoderma applanatum causaram as maiores perdas de massa, sem diferença significativa para o Gloeophyllum trabeum. A resina FF proporcionou maior resistência à ação dos fungos nas chapas OSB, o mesmo fato ocorrendo com o maior teor de resina. O fungo Coniophora puteana foi altamente sensível ao tipo de resina aplicado, enquanto o Bjerkandera fumosa demonstrou reduzida ação nas concentrações mais altas de ambas as resinas. O fungo Fomes annosus apresentou degradação insignificante para todos os tratamentos de chapas OSB. Palavras-chave durabilidade natural; fungos xilófagos; Hevea brasiliensis; OSB

© Copyright 2009 - Ciência Florestal
Alternative site location: http://cascavel.ufsm.br/revistas/ojs-2.2.2/index.php/cienciaflorestal/index